Low Cement Castable
Type : Lc-45
Application : Industrial Use
Color : Off White
Feature : Superior Resistance ..
Alumina Content : 45%
Type : Lc-60
Color : White
Form : Powder
Type : Lc-80
Color : Grey
From : Powder
Ferro Alloy
Shape : Lumps
Application : Industrial
Feature : High Composition
Texture : Hard
Material : Manganese
Color : Natural-grey
Form : Lumps
Size : As per customer’s ..
Other Products
SiO2 Content (%) : 98.5%
Grading : 0-5mm
Sintering Temp : 1200°C min & 1700°..
Setting Material : Ceramic
Packaging : 50kg Hdpe Bag
MgO Content(%) : >72%
Sintering Temp : 800°C min & 1750°C..
Setting : Ceramic Bonding
Grade : Technical Grade
Color : Z-black
Packaging Type : Plastic Barrels, Pla..
Feature : High Quality
Packaging Type : Hdpe Bag, Plastic Pa..
Sio2 : 30-33%
CaO : 28-30%
Al2O3 : 4-6%
MgO : 2-4%
Material : Silica Based
Shape : Rectangular
Color : Brown
Feature : Accurate Dimensions
Application : Refractory Material
Packaging Type : Plastic Bag, Plastic..
Packaging Size : 25 Kg, 50 Kg
Type : Slide Gate Plates
Al2O3 : 93.62%
MgO : 1.4%
Bulk Density : 3080kg/m3
Fixed Carbon : 4.52%
Type : Al2o3 – C Based No..
Al2O3 : 81.2%
Fe2O3 : 0.44%
Bulk Density : 2850kg/m3
Shelf Life : 12 months
Shelf Life : 12 Months
Shape : Round
Color : Black
Feature : Accurate Composition
Finishing : Polished
Type : Porous Plug
MgO : 95%
Apparent Porosity : 25.4%
Air Flow Rate At 0.4kg/cm2 : 60ltrs/min
Type : Alumina Based Seatin..
Al2O3 : 45.6%
Apparent Porosity : 19.8%
Bulk Density : 2220kg/m3
Type : Pressed Well Block &..
Al2O3 : 73.4%
Apparent Porosity : 8.5%
Bulk Density : 2890kg/m3
Material : Alumina
Shape : Square
Structure : Solid
Shape : Rectangular, Square
Type : Fired Hi-grade Alumi..
Al2O3 Content (%) : 45-90%
Type : Fire Bricks
Color : Brown, Red
Resistance Durability : Fire Resistance, Hea..
Hardness : 3-6mohs
Packaging Size : 25-50kg
Type : Al2o3 Mortar
Material : Magnesia Carbon